APTIV® 1100 Series Films (Polyetheretherketone)
Weitere Informationen finden Sie hier.
Symbolbild
- Electrical insulation
- Pressure sensor membranes
- Printed circuit substrates
- Acoustic speaker diaphragms
- High temperature labels
- Proven temperature resistance to use of lead free solders
- Flexible surface heaters
- gebräuchliche Bezeichnung: Polyetheretherketone
- Abkürzung: PEEK
- High heat resistance
- Low smoke and toxic gas emission
- Excellent acoustic properties
- Excellent hydrolysis resistance
- Broad chemical resistance
- Excellent barrier properties
- Low moisture absorption
- High strength and toughness
- High purity
- Stable, excellent electrical insulation properties
- Lightweight
- Good flammability performance without use of flame retardant additives
- Recyclable
- Inherently halogen-free
- Radiation resistance
- Easy to process – can be laminated to other materials, thermoformed, metallised, coated, printed, stamped and die cut, welded and heat sealed and coated.
- Improved thermal conductivity over APTIV 1000 film
Physikalische Eigenschaften
Name | Wert | Bemerkung | Messverfahren und -bedingungen |
---|---|---|---|
Dicke | 12 – 125 µm | ||
Flächenschrumpf | < 0.5 % | TM-VX-84, 200ºC (392°F), 1102-050M, MD | |
< 0.5 % | TM-VX-84, 200ºC (392°F), 1102-050M, TD | ||
< 0.5 % | TM-VX-84, 200ºC (392°F), 1103-050M, MD | ||
< 0.5 % | TM-VX-84, 200ºC (392°F), 1103-050M, TD | ||
relative Dichte | 1.45 | ISO 1183, 23ºC (73°F), 1102-050M | |
1.54 | ISO 1183, 23ºC (73°F), 1103-050M | ||
Wasseraufnahme | 0.08 % | 50% RH | ISO 62, 23ºC (73°F), 24h, 1102-050M |
0.09 % | 50% RH | ISO 62, 23ºC (73°F), 24h, 1103-050M | |
Mechanische Eigenschaften | |||
Weiterreißwiderstand | 6 N/mm | ISO 6383-1, 23ºC (73°F), 1102-050M, MD | |
7 N/mm | ISO 6383-1, 23ºC (73°F), 1102-050M, TD | ||
5 N/mm | ISO 6383-1, 23ºC (73°F), 1103-050M, MD | ||
6 N/mm | ISO 6383-1, 23ºC (73°F), 1103-050M, TD | ||
Zug-Elastizitätsmodul | 5 GPa | ISO 527, 23°C (73°F), 20% Mineral Filled, 25μm, MD | |
4.5 GPa | ISO 527, 23°C (73°F), 20% Mineral Filled, 25μm, TD | ||
4.8 GPa | ISO 527, 23°C (73°F), 20% Mineral Filled, 50μm, MD | ||
4.3 GPa | ISO 527, 23°C (73°F), 20% Mineral Filled, 50μm, TD | ||
4.5 GPa | ISO 527, 23°C (73°F), 20% Mineral Filled, 100μm, MD | ||
4.2 GPa | ISO 527, 23°C (73°F), 20% Mineral Filled100μm, TD | ||
5.5 GPa | ISO 527, 23°C (73°F), 30% Mineral Filled, 25μm, MD | ||
4.5 GPa | ISO 527, 23°C (73°F), 30% Mineral Filled, 25μm, TD | ||
5.5 GPa | ISO 527, 23°C (73°F), 30% Mineral Filled, 50μm, MD | ||
4.5 GPa | ISO 527, 23°C (73°F), 30% Mineral Filled, 50μm, TD | ||
5 GPa | ISO 527, 23°C (73°F), 30% Mineral Filled, 100μm, MD | ||
4.5 GPa | ISO 527, 23°C (73°F), 30% Mineral Filled, 100μm, TD | ||
Zugdehnung beim Bruch | > 100 % | ISO 527, 23°C (73°F), 20% Mineral Filled, 25μm, MD | |
> 10 % | ISO 527, 23°C (73°F), 20% Mineral Filled, 25μm, TD | ||
> 100 % | ISO 527, 23°C (73°F), 20% Mineral Filled, 50μm, MD | ||
> 10 % | ISO 527, 23°C (73°F), 20% Mineral Filled, 50μm, TD | ||
> 100 % | ISO 527, 23°C (73°F), 20% Mineral Filled, 100μm, MD | ||
> 10 % | ISO 527, 23°C (73°F), 20% Mineral Filled, 100μm, TD | ||
> 10 % | ISO 527, 23°C (73°F), 30% Mineral Filled, 25μm, MD | ||
> 10 % | ISO 527, 23°C (73°F), 30% Mineral Filled, 25μm, TD | ||
> 10 % | ISO 527, 23°C (73°F), 30% Mineral Filled, 50μm, MD | ||
> 10 % | ISO 527, 23°C (73°F), 30% Mineral Filled, 50μm, TD | ||
> 5 % | ISO 527, 23°C (73°F), 30% Mineral Filled, 100μm, MD | ||
> 10 % | ISO 527, 23°C (73°F), 30% Mineral Filled, 100μm, TD | ||
Zugfestigkeit | 100 MPa | ISO 527, at break, 23°C (73°F), 20% Mineral Filled, 25μm, MD | |
80 MPa | ISO 527, at break, 23°C (73°F), 20% Mineral Filled, 25μm, TD | ||
100 MPa | ISO 527, at break, 23°C (73°F), 20% Mineral Filled, 50μm, MD | ||
80 MPa | ISO 527, at break, 23°C (73°F), 20% Mineral Filled, 50μm, TD | ||
100 MPa | ISO 527, at break, 23°C (73°F), 20% Mineral Filled, 100μm, MD | ||
80 MPa | ISO 527, at break, 23°C (73°F), 20% Mineral Filled, 100μm, TD | ||
70 MPa | ISO 527, at break, 23°C (73°F), 30% Mineral Filled, 25μm, MD | ||
70 MPa | ISO 527, at break, 23°C (73°F), 30% Mineral Filled, 25μm, TD | ||
90 MPa | at break, 23°C (73°F), 30% Mineral Filled, 50μm, MD | ||
90 MPa | at break, 23°C (73°F), 30% Mineral Filled, 50μm, TD | ||
90 MPa | at break, 23°C (73°F), 30% Mineral Filled, 100μm, MD | ||
90 MPa | at break, 23°C (73°F), 30% Mineral Filled, 100μm, TD | ||
Elektrische und magnetische Eigenschaften | |||
dielektrischer Verlustfaktor | 0.001 | ASTM D150, 23ºC (73°F), 10 MHz | |
Durchschlagfestigkeit | 200 kV/mm | ATSM D149, 23°C (73°F), 6.25mm (0.25in) electrode, 1102-050M | |
200 kV/mm | ATSM D149, 23°C (73°F), 6.25mm (0.25in) electrode, 1103-050M | ||
spezifischer Durchgangswiderstand | 1.0E+16 Ω*cm | ASTM D257, 23ºC (73°F), 100V, 1102-050M | |
1.0E+16 Ω*cm | ASTM D257, 23ºC (73°F), 100V, 1103-050M | ||
Thermische Eigenschaften | |||
linearer Längenausdehnungskoeffizient | 35 ppm/°C | ASTM D696, MD, below Tg, 1102-050M | |
18 ppm/°C | ASTM D696, MD, below Tg, 1103-050M |
Freigaben
Regularium | Land | Bauteil | Bemerkungen | Gültig bis | Prüfzeugnis |
---|---|---|---|---|---|
FDA 21 CFR 177.2415 | compliant with the compositional requirements | ||||
1935/2004/EC | compliant | ||||
2002/72/EC | compliant | ||||
2005/79/EC | compliant | ||||
RoHS 2002/95/EC | complies with the requirements | ||||
IEC61249-2-21 | inherently halogen-free in accordance with |
Daten bereitgestellt von
Victrex plc
+(44) 1253 897700
Anfrage per E-Mail
Webseite | Mehr Details | Zu den Materialien von Victrex plc
Victrex plc and/or its group companies (“Victrex plc”) believes that the information contained in this document is an accurate description of the typical characteristics and/or uses of the product or products, but it is the customer’s responsibility to thoroughly test the product in each specific application to determine its performance, efficacy, and safety for each end-use product, device or other application. Suggestions of uses should not be taken as inducements to infringe any particular patent. The information and data contained herein are based on information we believe reliable. Mention of a product in this document is not a guarantee of availability. Victrex plc reserves the right to modify products, specifications and/or packaging as part of a continuous program of product development. Victrex plc makes no warranties, express or implied, including, without limitation, a warranty of fitness for a particular purpose or of intellectual property non-infringement, including, but not limited to patent non-infringement, which are expressly disclaimed, whether express or implied, in fact or by law. Further, Victrex plc makes no warranty to your customers or agents, and has not authorized anyone to make any representation or warranty other than as provided above. Victrex plc shall in no event be liable for any general, indirect, special, consequential, punitive, incidental or similar damages, including without limitation, damages for harm to business, lost profits or lost savings, even if Victrex has been advised of the possibility of such damages regardless of the form of action. VICTREX™, APTIV™, VICOTE™, VICTREX PIPES™, VICTREX HT™, VICTREX ST™, VICTREX WG™, PEEK-ESD™ and the Triangle (Device), are trademarks of Victrex plc or its group companies.
Ähnliche Materialien
Wählen Sie die Materialeigenschaften aus, anhand derer ähnliche Materialien identifiziert werden sollen. Durch Hinzufügen weiterer Eigenschaften sowie Anpassen der jeweiligen Abweichung lässt sich die Ergebnisliste beeinflussen. Hier wird eine Auswahl der ähnlichsten Materialien angezeigt. Um die gesamte Liste zu erhalten, drücken Sie auf die Schaltfläche "Vollständige Ergebnisliste anzeigen".