Key to Metals AG (Datenlieferant)
Aluminium 7075 (SAE)
Weitere Informationen finden Sie hier.
Symbolbild
Einsatzbeispiele
- For parts requiring forming and as stock for flash welded rings which are to be subsequently solution and precipitation heat treated.
- Parts requiring a combination of good strength and resistance to stress-corrosion cracking, but usage is not limited to such applications.
- Parts requiring high strength and resistance to stress-corrosion cracking, but usage is not limited to such applications.
- Parts requiring high strength and whose fabrication does not usually involve welding or forming, but usage is not limited to such applications.
- Parts subject to excessive warpage during machining and for parts requiring high strength and resistance to stress-corrosion cracking, but usage is not limited to such applications.
- Structural components, including machined par ts subject to excessive warpage during machining, but usage is not limited to such applications.
- These products have been used typically for formed structural parts which will be subsequently heat treated, but usage is not limited to such applications.
- These products have been used typically for machined parts subject to excessive warpage during machining due to residual stresses and for parts requiring high strength and resistance to stress-corrosion cracking and whose fabrication does not involve forming or welding, but usage is not limited to such applications.
- These products have been used typically for machined parts subject to excessive warpage during machining due to residual stresses and for parts requiring high strength and whose fabrication does not involve welding or forming, but usage is not limited to such applications.
- These products have been used typically for parts requiring high strength and resistance to stress-corrosion cracking, but usage is not limited to such applications.
- These products have been used typically for parts subject to excessive warpage during machining and for parts requiring high strength and whose fabrication does not involve welding or forming, but usage is not limited to such applications.
- These rings have been used typically for applications requiring a combination of high strength, resistance to stresscorrosion cracking, and good stability during machining, but usage is not limited to such applications.
- These rings have been used typically for high strength machined parts where good stability is required during machining, but usage is not limited to such applications. These rings are not recommended for fusion welding.
- These rings have been used typically for parts requiring high strength and resistance to stress-corrosion cracking, but usage is not limited to such applications.
- This product has been used typically for structural applications requiring material with high strength and resistance to exfoliation-corrosion, but usage is not limited to such applications.
- This sheet has been used typically for severely formed structural parts which will be subsequently heat treated and painted or otherwise protected from corrosion, but usage is not limited to such applications.
- Used for parts requiring forming and as stock for flash welded rings which are to be subsequently solution and precipitation heat treated, but usage is not limited to such applications.
- Used for small and medium size forgings where maximum weight saving is essential.
- Used for small and medium sized forgings where maximum weight saving is essential. Special care should be taken in the application of this alloy in temper other than T73 because of susceptibility to stress-corrosion cracking.
- Used typically for applications requiring high strength in light-to-medium sections, but usage is not limited to such applications.
- Used typically for parts requiring a combination of good strength and resistance to stress-corrosion cracking, and where good stability is required during machining, but usage is not limited to such applications.
- Used typically for parts requiring a high level of mechanical properties and good resistance to stress-corrosion cracking, but usage is not limited to such applications.
- Used typically for parts requiring good resistance to stress-corrosion cracking but with lower strength than AMS4126, but usage is not limited to such applications.
- Used typically for parts requiring high strength after heat treatment and whose fabrication does not involve welding or forming, but usage is not limited to such applications
- Used typically for parts requiring high strength where limited formability is acceptable.
- Used typically for structural applications requiring material with high strength and resistance to exfoliation-corrosion, but usage is not limited to such applications.
Bauwesen; Fahrzeugbau; Farbenindustrie; Fördertechnik; Mechanik
Physikalische Eigenschaften
| Name | Wert | Messverfahren und -bedingungen |
|---|---|---|
| Dichte | 2.796 kg/dm³ | |
| Mechanische Eigenschaften | ||
| 0,2-%-Streckgrenze bei Zugbeanspruchung | 66 – 530.8 MPa | |
| Schubmodul | 26 – 28 GPa | |
| Zug-Elastizitätsmodul | 69 – 72 GPa | |
| Zugdehnung beim Bruch | > 1 % | |
| Zugfestigkeit | 75 – 586 MPa | |
| Elektrische und magnetische Eigenschaften | ||
| spezifischer elektrischer Widerstand | 0.052 Ω∙mm²/m | |
| Thermische Eigenschaften | ||
| spezifische Wärmekapazität | 825.48 – 843.153 J/(kg∙°C) | |
| Wärmeleitfähigkeit | 129.805 – 155.66 W/(m∙°C) | |
Daten bereitgestellt von
Key to Metals AG
IBDT Ingenieurbüro Daniel Trost
+49 176 703 22 119
Anfrage per E-Mail
Webseite | Mehr Details | Zu den Materialien von Key to Metals AG
Ähnliche Materialien
Wählen Sie die Materialeigenschaften aus, anhand derer ähnliche Materialien identifiziert werden sollen. Durch Hinzufügen weiterer Eigenschaften sowie Anpassen der jeweiligen Abweichung lässt sich die Ergebnisliste beeinflussen. Hier wird eine Auswahl der ähnlichsten Materialien angezeigt. Um die gesamte Liste zu erhalten, drücken Sie auf die Schaltfläche "Vollständige Ergebnisliste anzeigen".