Key to Metals AG (Datenlieferant)
8630 (SAE)
Weitere Informationen finden Sie hier.
Symbolbild
Einsatzbeispiele
- These products have been used typically for parts, with sections 0.500 inch (12.70 mm) and under in thickness at time of heat treatment, requiring a through-hardening steel capable of developing hardness as high as 35 HRC when properly hardened and tempered and also for parts of greater thickness but requiring proportionately lower hardness, but usage is not limited to such applications.
- Used typically for parts, with section thickness of 12.7 mm and under at time of heat treatment, requiring a through-hardening steel capable of developing hardness as high as 35 HRC, and for parts of greater thickness requiring proportionately lower hardness, but usage is not limited to such applications.
Portionieren
Physikalische Eigenschaften
| Name | Wert | Messverfahren und -bedingungen |
|---|---|---|
| Dichte | 7.833 kg/dm³ | |
| Mechanische Eigenschaften | ||
| 0,2-%-Streckgrenze bei Zugbeanspruchung | > 482 MPa | |
| Schlagenergie | 25.7 – 53.2 J | |
| Schubmodul | 76 GPa | |
| Zug-Elastizitätsmodul | 200 GPa | |
| Zugdehnung beim Bruch | > 8 % | |
| Zugfestigkeit | 586 – 1379 MPa | |
Daten bereitgestellt von
Key to Metals AG
IBDT Ingenieurbüro Daniel Trost
+49 176 703 22 119
Anfrage per E-Mail
Webseite | Mehr Details | Zu den Materialien von Key to Metals AG
Ähnliche Materialien
Wählen Sie die Materialeigenschaften aus, anhand derer ähnliche Materialien identifiziert werden sollen. Durch Hinzufügen weiterer Eigenschaften sowie Anpassen der jeweiligen Abweichung lässt sich die Ergebnisliste beeinflussen. Hier wird eine Auswahl der ähnlichsten Materialien angezeigt. Um die gesamte Liste zu erhalten, drücken Sie auf die Schaltfläche "Vollständige Ergebnisliste anzeigen".