Key to Metals AG (Datenlieferant)
52100 (SAE)
Weitere Informationen finden Sie hier.
Symbolbild
Einsatzbeispiele
- Used typically for bearing components requiring a through-hardening steel usually with hardness of approximately 60 HRC, section thickness under 12.7 mm, and subject to very rigid inspection standards, but usage is not limited to such applications.
- Used typically for bearing components requiring a through-hardening steel, usually with hardness of approximately 60 HRC and section thickness under 12.7 mm, but usage is not limited to such applications.
- Used typically for parts requiring a through-hardening steel, usually with hardness of approximately 60 HRC in section thicknesses 12.7 mm (0.50 inch) and under, and subject to very rigid inspection standards, but usage is not limited to such applications.
- Used typically for parts requiring a through-hardening steel, usually with hardness of approximately 60 HRC in section thicknesses 12.7 mm and under, and subject to very rigid inspection standards, but usage is not limited to such applications.
Lager
Physikalische Eigenschaften
| Name | Wert | Messverfahren und -bedingungen |
|---|---|---|
| Mechanische Eigenschaften | ||
| Zugfestigkeit | < 827 MPa | |
Daten bereitgestellt von
Key to Metals AG
IBDT Ingenieurbüro Daniel Trost
+49 176 703 22 119
Anfrage per E-Mail
Webseite | Mehr Details | Zu den Materialien von Key to Metals AG
Ähnliche Materialien
Wählen Sie die Materialeigenschaften aus, anhand derer ähnliche Materialien identifiziert werden sollen. Durch Hinzufügen weiterer Eigenschaften sowie Anpassen der jeweiligen Abweichung lässt sich die Ergebnisliste beeinflussen. Hier wird eine Auswahl der ähnlichsten Materialien angezeigt. Um die gesamte Liste zu erhalten, drücken Sie auf die Schaltfläche "Vollständige Ergebnisliste anzeigen".