4135 (SAE)
Weitere Informationen finden Sie hier.
Symbolbild
- These products have been used typically for heat treated parts and structures that may require welding during fabrication, but usage is not limited to such applications. It may be through -hardened to a minimum tensile strength of 180 ksi (1241 MPa) in sections 0.125 inch (3.18 mm) and under in nominal thickness and proportionately lower strength in heavier section thicknesses
- This tubing has been used typically for parts, 19 mm and under in section thickness at time of heat treatment, requiring a through-hardening steel capable of developing hardness as high as 40 HRC when properly hardened and tempered and for parts of greater thickness but requiring proportionately lower hardness, but usage is not limited to such applications.
- This tubing has been used typically for thin wall-thickness sections where minimum tensile strength up to 1103 MPa is required and where parts may be welded during fabrication, but usage is not limited to such applications.
Physikalische Eigenschaften
Name | Wert | Messverfahren und -bedingungen |
---|---|---|
Dichte | 7.833 kg/dm³ | |
Mechanische Eigenschaften | ||
0,2-%-Streckgrenze bei Zugbeanspruchung | > 482.6 MPa | |
Schubmodul | 76 GPa | |
Zug-Elastizitätsmodul | 200 GPa | |
Zugdehnung beim Bruch | > 4 % | |
Zugfestigkeit | 620.5 – 1379 MPa |
Daten bereitgestellt von
Key to Metals AG
IBDT Ingenieurbüro Daniel Trost
+49 176 703 22 119
Anfrage per E-Mail
Webseite | Mehr Details | Zu den Materialien von Key to Metals AG
Ähnliche Materialien
Wählen Sie die Materialeigenschaften aus, anhand derer ähnliche Materialien identifiziert werden sollen. Durch Hinzufügen weiterer Eigenschaften sowie Anpassen der jeweiligen Abweichung lässt sich die Ergebnisliste beeinflussen. Hier wird eine Auswahl der ähnlichsten Materialien angezeigt. Um die gesamte Liste zu erhalten, drücken Sie auf die Schaltfläche "Vollständige Ergebnisliste anzeigen".