Institut für Holztechnologie Dresden gemeinnützige GmbH (Datenlieferant)
Particleboard P7
Symbolbild
alternative Namen
- Deutsch: Spanplatte
- Deutsch: Flachpressplatte
- Englisch: Particleboard
- Englisch: Chipboard
- Englisch: Low-Density Fibreboard
- Englisch: Low-Density Fiberboard
Versuchsaufbau
- Characteristic Values of wood based panels are 5-percentiles for strength values (f) and mean values for elastic properties (E, G). If necessary the 5-percentile values of the elastic properties can be calculated as 0.85 times the specified mean values.
- Indices are given in the following way:
- 1st index: indicates bending, tension, compression, shear or rolling shear as “m”, “t”, “c”, “v” or “r”
- 2nd index: indicates orientation of stress to grain direction of outermost layers/veneers as “0” or”90”, if relevant
- 3rd index: indicates, if in plane or out of plane; in plane is given as “edge”, out of plane is given as “flat” only in the case of stresses perpendicular to the grain and shear
- 4th index: indicates characteristic “k” or mean value “mean”
Physikalische Eigenschaften
| Name | Wert | Bemerkung | Messverfahren und -bedingungen |
|---|---|---|---|
| Dichte | > 650 kg/m³ | nominal thickness: > 6mm – 13mm | DIN EN 12369-1 |
| > 600 kg/m³ | nominal thickness: > 13mm – 20mm | DIN EN 12369-1 | |
| > 550 kg/m³ | nominal thickness: > 20mm – 25mm | DIN EN 12369-1 | |
| > 550 kg/m³ | nominal thickness: > 25mm – 32mm | DIN EN 12369-1 | |
| > 500 kg/m³ | nominal thickness: > 32mm – 40mm | DIN EN 12369-1 | |
| Modifikationsbeiwert | 0.4 | Service Class 1 | DIN EN 312; DIN EN 1995-1-1, permanent |
| 0.5 | Service Class 1 | DIN EN 312; DIN EN 1995-1-1, long term | |
| 0.7 | Service Class 1 | DIN EN 312; DIN EN 1995-1-1, medium term | |
| 0.9 | Service Class 1 | DIN EN 312; DIN EN 1995-1-1, short term | |
| 1.1 | Service Class 1 | DIN EN 312; DIN EN 1995-1-1, instantaneous | |
| 0.3 | Service Class 2 | DIN EN 312; DIN EN 1995-1-1, permanent | |
| 0.4 | Service Class 2 | DIN EN 312; DIN EN 1995-1-1, long term | |
| 0.55 | Service Class 2 | DIN EN 312; DIN EN 1995-1-1, medium term | |
| 0.7 | Service Class 2 | DIN EN 312; DIN EN 1995-1-1, short term | |
| 0.9 | Service Class 2 | DIN EN 312; DIN EN 1995-1-1, instantaneous | |
| Verformungsbeiwert | 1.5 | Service Class 1 | DIN EN 312; DIN EN 1995-1-1 |
| 2.25 | Service Class 2 | DIN EN 312; DIN EN 1995-1-1 | |
| Wasserdampf-Diffusionswiderstandszahl | 10 | wet cup µ | DIN EN 13986; DIN EN 312, density: 300 kg/m³ |
| 50 | dry cup µ | DIN EN 13986; DIN EN 312, density: 300 kg/m³ | |
| 15 | wet cup µ | DIN EN 13986; DIN EN 312, density: 600 kg/m³ | |
| 50 | dry cup µ | DIN EN 13986; DIN EN 312, density: 600 kg/m³ | |
| 20 | wet cup µ | DIN EN 13986; DIN EN 312, density: 900 kg/m³ | |
| 50 | dry cup µ | DIN EN 13986; DIN EN 312, density: 900 kg/m³ | |
| Mechanische Eigenschaften | |||
| Biege-Elastizitätsmodul | 4600 MPa | nominal thickness: > 6mm – 13mm | DIN EN 12369-1, E[m,flat,mean] (perpendicular to plane) |
| 4200 MPa | nominal thickness: > 13mm – 20mm | DIN EN 12369-1, E[m,flat,mean] (perpendicular to plane) | |
| 4000 MPa | nominal thickness: > 20mm – 25mm | DIN EN 12369-1, E[m,flat,mean] (perpendicular to plane) | |
| 3900 MPa | nominal thickness: > 25mm – 32mm | DIN EN 12369-1, E[m,flat,mean] (perpendicular to plane) | |
| 3500 MPa | nominal thickness: > 32mm – 40mm | DIN EN 12369-1, E[m,flat,mean] (perpendicular to plane) | |
| Biegefestigkeit | 18.3 MPa | nominal thickness: > 6mm – 13mm | DIN EN 12369-1, f[m,k] (perpendicular to plane) |
| 16.7 MPa | nominal thickness: > 13mm – 20mm | DIN EN 12369-1, f[m,k] (perpendicular to plane) | |
| 15.4 MPa | nominal thickness: > 20mm – 25mm | DIN EN 12369-1, f[m,k] (perpendicular to plane) | |
| 14.2 MPa | nominal thickness: > 25mm – 32mm | DIN EN 12369-1, f[m,k] (perpendicular to plane) | |
| 13.3 MPa | nominal thickness: > 32mm – 40mm | DIN EN 12369-1, f[m,k] (perpendicular to plane) | |
| Druck-Elastizitätsmodul | 2600 MPa | nominal thickness: > 6mm – 13mm | DIN EN 12369-1, E[c,edge,mean] (in plane) |
| 2500 MPa | nominal thickness: > 13mm – 20mm | DIN EN 12369-1, E[c,edge,mean] (in plane) | |
| 2400 MPa | nominal thickness: > 20mm – 25mm | DIN EN 12369-1, E[c,edge,mean] (in plane) | |
| 2300 MPa | nominal thickness: > 25mm – 32mm | DIN EN 12369-1, E[c,edge,mean] (in plane) | |
| 2100 MPa | nominal thickness: > 32mm – 40mm | DIN EN 12369-1, E[c,edge,mean] (in plane) | |
| Druckfestigkeit | 15.5 MPa | nominal thickness: > 6mm – 13mm | DIN EN 12369-1, f[c,edge,k] (in plane) |
| 14.7 MPa | nominal thickness: > 13mm – 20mm | DIN EN 12369-1, f[c,edge,k] (in plane) | |
| 13.7 MPa | nominal thickness: > 20mm – 25mm | DIN EN 12369-1, f[c,edge,k] (in plane) | |
| 13.5 MPa | nominal thickness: > 25mm – 32mm | DIN EN 12369-1, f[c,edge,k] (in plane) | |
| 13.2 MPa | nominal thickness: > 32mm – 40mm | DIN EN 12369-1, f[c,edge,k] (in plane) | |
| Scherfestigkeit | 8.6 MPa | nominal thickness: > 6mm – 13mm | DIN EN 12369-1, f[v,edge,k] (perpendicular to plane) |
| 2.4 MPa | nominal thickness: > 6mm – 13mm | DIN EN 12369-1, f[v,flat,k] (in plane) | |
| 8.1 MPa | nominal thickness: > 13mm – 20mm | DIN EN 12369-1, f[v,edge,k] (perpendicular to plane) | |
| 2.2 MPa | nominal thickness: > 13mm – 20mm | DIN EN 12369-1, f[v,flat,k] (in plane) | |
| 7.9 MPa | nominal thickness: > 20mm – 25mm | DIN EN 12369-1, f[v,edge,k] (perpendicular to plane) | |
| 2 MPa | nominal thickness: > 20mm – 25mm | DIN EN 12369-1, f[v,flat,k] (in plane) | |
| 7.4 MPa | nominal thickness: > 25mm – 32mm | DIN EN 12369-1, f[v,edge,k] (perpendicular to plane) | |
| 1.9 MPa | nominal thickness: > 25mm – 32mm | DIN EN 12369-1, f[v,flat,k] (in plane) | |
| 7.2 MPa | nominal thickness: > 32mm – 40mm | DIN EN 12369-1, f[v,edge,k] (perpendicular to plane) | |
| 1.9 MPa | nominal thickness: > 32mm – 40mm | DIN EN 12369-1, f[v,flat,k] (in plane) | |
| Schubmodul | 1250 MPa | nominal thickness: > 6mm – 13mm | DIN EN 12369-1, G[edge,mean] (perpendicular to plane) |
| 1200 MPa | nominal thickness: > 13mm – 20mm | DIN EN 12369-1, G[edge,mean] (perpendicular to plane) | |
| 1150 MPa | nominal thickness: > 20mm – 25mm | DIN EN 12369-1, G[edge,mean] (perpendicular to plane) | |
| 1100 MPa | nominal thickness: > 25mm – 32mm | DIN EN 12369-1, G[edge,mean] (perpendicular to plane) | |
| 1050 MPa | nominal thickness: > 32mm – 40mm | DIN EN 12369-1, G[edge,mean] (perpendicular to plane) | |
| Zug-Elastizitätsmodul | 2600 MPa | nominal thickness: > 6mm – 13mm | DIN EN 12369-1, E[t,mean] |
| 2500 MPa | nominal thickness: > 13mm – 20mm | DIN EN 12369-1, E[t,mean] | |
| 2400 MPa | nominal thickness: > 20mm – 25mm | DIN EN 12369-1, E[t,mean] | |
| 2300 MPa | nominal thickness: > 25mm – 32mm | DIN EN 12369-1, E[t,mean] | |
| 2100 MPa | nominal thickness: > 32mm – 40mm | DIN EN 12369-1, E[t,mean] | |
| Zugfestigkeit | 11.5 MPa | nominal thickness: > 6mm – 13mm | DIN EN 12369-1, f[t,k] |
| 10.6 MPa | nominal thickness: > 13mm – 20mm | DIN EN 12369-1, f[t,k] | |
| 9.8 MPa | nominal thickness: > 20mm – 25mm | DIN EN 12369-1, f[t,k] | |
| 9.4 MPa | nominal thickness: > 25mm – 32mm | DIN EN 12369-1, f[t,k] | |
| 9 MPa | nominal thickness: > 32mm – 40mm | DIN EN 12369-1, f[t,k] | |
| Thermische Eigenschaften | |||
| Wärmeleitfähigkeit | 0.07 W/(m*K) | DIN EN 13986; DIN EN 312, density: 300 kg/m³ | |
| 0.12 W/(m*K) | DIN EN 13986; DIN EN 312, density: 600 kg/m³ | ||
| 0.18 W/(m*K) | DIN EN 13986; DIN EN 312, density: 900 kg/m³ | ||
Daten bereitgestellt von
Institut für Holztechnologie Dresden gemeinnützige GmbH
Institut für Holztechnologie Dresden gemeinnützige GmbH Steffen Tobisch
+493514662257
Anfrage per E-Mail
Webseite | Mehr Details | Zu den Materialien von Institut für Holztechnologie Dresden gGmbH
Haftungsausschluss
Die in diesem Dokument enthaltenen Informationen und Daten wurden entweder durch Prüfungen, Berechnungen oder Bewertungen vom Datenanbieter ermittelt und werden als korrekt erachtet. Die aufgeführten Werte sind jedoch beeinflussbar durch Verarbeitungsbedingungen, Modifikationen, Werkstoffzusätze und Umgebungseinflüsse und befreien den Anwender nicht von eigenen Prüfungen und Versuchen. Eine rechtlich verbindliche Zusicherung bestimmter Eigenschaften oder der Eignung für einen konkreten, insbesondere sicherheitsrelevanten Einsatzzweck durch den Datenanbieter kann aus den Angaben nicht abgeleitet werden.
Ähnliche Materialien
Wählen Sie die Materialeigenschaften aus, anhand derer ähnliche Materialien identifiziert werden sollen. Durch Hinzufügen weiterer Eigenschaften sowie Anpassen der jeweiligen Abweichung lässt sich die Ergebnisliste beeinflussen. Hier wird eine Auswahl der ähnlichsten Materialien angezeigt. Um die gesamte Liste zu erhalten, drücken Sie auf die Schaltfläche "Vollständige Ergebnisliste anzeigen".