Institut für Holztechnologie Dresden gemeinnützige GmbH (Datenanbieter)

Oriented Strand Board OSB/4

Symbolbild

alternative Namen
  • Abkürzung: OSB
  • Deutsch: Grobspanplatte
  • Englisch: Oriented Strand Board
  • Englisch: Oriented Structural Board
Versuchsaufbau
  • Characteristic Values of wood based panels are 5-percentiles for strength values (f) and mean values for elastic properties (E, G). If necessary the 5-percentile values of the elastic properties can be calculated as 0.85 times the specified mean values.
  • Indices are given in the following way:
  • 1st index: indicates bending, tension, compression, shear or rolling shear as “m”, “t”, “c”, “v” or “r”
  • 2nd index: indicates orientation of stress to grain direction of outermost layers/veneers as “0” or”90”, if relevant
  • 3rd index: indicates, if in plane or out of plane; in plane is given as “edge”, out of plane is given as “flat” only in the case of stresses perpendicular to the grain and shear
  • 4th index: indicates characteristic “k” or mean value “mean”

Physikalische Eigenschaften

Name Wert Bemerkung Messverfahren und -bedingungen
Dichte > 550 kg/m³ nominal thickness: > 6mm – 25mm prEN 12369-3
Differentielle Schwindung 0.74 – 1.2 %/% thickness
0.037 – 0.067 %/% length
0.015 – 0.032 %/% width
Gleichgewichtsfeuchte 6.6 – 7.5 % relative humidity: 30 %
8.9 – 9.8 % relative humidity: 65 %
15.4 – 16.2 % relative humidity: 85 %
Modifikationsbeiwert 0.4 Service Class 1 DIN EN 300; DIN EN 1995-1-1, permanent
0.5 Service Class 1 DIN EN 300; DIN EN 1995-1-1, long term
0.7 Service Class 1 DIN EN 300; DIN EN 1995-1-1, medium term
0.9 Service Class 1 DIN EN 300; DIN EN 1995-1-1, short term
1.1 Service Class 1 DIN EN 300; DIN EN 1995-1-1, instantaneous
0.3 Service Class 2 DIN EN 300; DIN EN 1995-1-1, permanent
0.4 Service Class 2 DIN EN 300; DIN EN 1995-1-1, long term
0.55 Service Class 2 DIN EN 300; DIN EN 1995-1-1, medium term
0.7 Service Class 2 DIN EN 300; DIN EN 1995-1-1, short term
0.9 Service Class 2 DIN EN 300; DIN EN 1995-1-1, instantaneous
Verformungsbeiwert 1.5 Service Class 1 DIN EN 300; DIN EN 1995-1-1
2.25 Service Class 1 DIN EN 300; DIN EN 1995-1-1
Mechanische Eigenschaften
 
Biege-Elastizitätsmodul 6780 MPa nominal thickness: > 6mm – 25mm prEN 12369-3, E[m,0,flat,mean] (perpendicular to plane)
2680 MPa nominal thickness: > 6mm – 25mm prEN 12369-3, E[m,90,flat,mean] (perpendicular to plane)
3900 MPa nominal thickness: > 6mm – 25mm E[m,0,edge,mean] (in plane)
3100 MPa nominal thickness: > 6mm – 25mm E[m,90,edge,mean] (in plane)
Biegefestigkeit 24.5 MPa nominal thickness: > 6mm – 10mm prEN 12369-3, f[m,0,k] (perpendicular to plane)
13 MPa nominal thickness: > 6mm – 10mm prEN 12369-3, f[m,90,k] (perpendicular to plane)
19.3 MPa nominal thickness: > 6mm – 10mm f[m,0,edge,k] (in plane)
15.8 MPa nominal thickness: > 6mm – 10mm f[m,90,edge,k] (in plane)
23 MPa nominal thickness: > 10mm – 18mm prEN 12369-3, f[m,0,k] (perpendicular to plane)
12.2 MPa nominal thickness: > 10mm – 18mm prEN 12369-3, f[m,90,k] (perpendicular to plane)
19.3 MPa nominal thickness: > 10mm – 18mm f[m,0,edge,k] (in plane)
15.8 MPa nominal thickness: > 10mm – 18mm f[m,90,edge,k] (in plane)
21 MPa nominal thickness: > 18mm – 25mm prEN 12369-3, f[m,0,k] (perpendicular to plane)
11.4 MPa nominal thickness: > 18mm – 25mm prEN 12369-3, f[m,90,k] (perpendicular to plane)
18.3 MPa nominal thickness: > 18mm – 25mm f[m,0,edge,k] (in plane)
15.8 MPa nominal thickness: > 18mm – 25mm f[m,90,edge,k] (in plane)
Druck-Elastizitätsmodul 4300 MPa nominal thickness: > 6mm – 25mm prEN 12369-3, E[c,0,mean] (in plane)
3200 MPa nominal thickness: > 6mm – 25mm prEN 12369-3, E[c,90,edge,mean] (in plane)
Druckfestigkeit 10 MPa nominal thickness: > 6mm – 25mm prEN 12369-3, f[c,0,90,flat,k] (perpendicular to plane)
18.1 MPa nominal thickness: > 6mm – 10mm prEN 12369-3, f[c,0,k] (in plane)
14.3 MPa nominal thickness: > 6mm – 10mm prEN 12369-3, f[c,90,edge,k] (in plane)
17.6 MPa nominal thickness: > 10mm – 18mm prEN 12369-3, f[c,0,k] (in plane)
14 MPa nominal thickness: > 10mm – 18mm prEN 12369-3, f[c,90,edge,k] (in plane)
17 MPa nominal thickness: > 18mm – 25mm prEN 12369-3, f[c,0,k] (in plane)
13.7 MPa nominal thickness: > 18mm – 25mm prEN 12369-3, f[c,90,edge,k] (in plane)
Scherfestigkeit 6.9 MPa nominal thickness: > 6mm – 25mm prEN 12369-3, f[v,0,90,edge,k] (perpendicular to plane)
1.1 MPa nominal thickness: > 6mm – 25mm prEN 12369-3, f[v,0,90,flat,k] (in plane)
Schubmodul 1090 MPa nominal thickness: > 6mm – 25mm prEN 12369-3, G[0,90,edge,mean] (perpendicular to plane)
60 MPa nominal thickness: > 6mm – 25mm prEN 12369-3, G[0,90,flat,mean] (in plane)
Zug-Elastizitätsmodul 4300 MPa nominal thickness: > 6mm – 25mm prEN 12369-3, E[t,0,mean]
3200 MPa nominal thickness: > 6mm – 25mm prEN 12369-3, E[t,90,edge,mean]
Zugfestigkeit 11.9 MPa nominal thickness: > 6mm – 10mm prEN 12369-3, f[t,0,k]
8.5 MPa nominal thickness: > 6mm – 10mm prEN 12369-3, f[t,90,edge,k]
11.4 MPa nominal thickness: > 10mm – 18mm prEN 12369-3, f[t,0,k]
8.2 MPa nominal thickness: > 10mm – 18mm prEN 12369-3, f[t,90,edge,k]
10.9 MPa nominal thickness: > 18mm – 25mm prEN 12369-3, f[t,0,k]
8 MPa nominal thickness: > 18mm – 25mm prEN 12369-3, f[t,90,edge,k]
Thermische Eigenschaften
 
Wärmeleitfähigkeit 0.13 W/(m*K) DIN EN 13986, density: 650 kg/m³

Daten bereitgestellt von

Institut für Holztechnologie Dresden gemeinnützige GmbH

Institut für Holztechnologie Dresden gemeinnützige GmbH Steffen Tobisch
+493514662257
Anfrage per E-Mail

Haftungsausschluss

Die in diesem Dokument enthaltenen Informationen und Daten wurden entweder durch Prüfungen, Berechnungen oder Bewertungen vom Datenanbieter ermittelt und werden als korrekt erachtet. Die aufgeführten Werte sind jedoch beeinflussbar durch Verarbeitungsbedingungen, Modifikationen, Werkstoffzusätze und Umgebungseinflüsse und befreien den Anwender nicht von eigenen Prüfungen und Versuchen. Eine rechtlich verbindliche Zusicherung bestimmter Eigenschaften oder der Eignung für einen konkreten, insbesondere sicherheitsrelevanten Einsatzzweck durch den Datenanbieter kann aus den Angaben nicht abgeleitet werden.

Ähnliche Materialien

Wählen Sie die Materialeigenschaften aus, anhand derer ähnliche Materialien identifiziert werden sollen. Durch Hinzufügen weiterer Eigenschaften sowie Anpassen der jeweiligen Abweichung lässt sich die Ergebnisliste beeinflussen. Hier wird eine Auswahl der ähnlichsten Materialien angezeigt. Um die gesamte Liste zu erhalten, drücken Sie auf die Schaltfläche "Vollständige Ergebnisliste anzeigen".

5%

Letzte Aktualisierung: 31.08.2023
Feedback

Geben Sie uns gern Feedback zum Material Hub.

Kontaktformular

Fragebogen zur Gebrauchstauglichkeit

QR Code