Material Hub > Materialien

Institut für Holztechnologie Dresden gemeinnützige GmbH (Datenanbieter)

Medium-Density Fibreboard MDF.LA

Symbolbild

alternative Namen
  • Abkürzung: MDF, MDF.LA
  • Deutsch: Mitteldichte Holzfaserplatte
  • Englisch: Medium-Density Fibreboard
  • Englisch: Medium-Density Fiberboard
Versuchsaufbau
  • Characteristic Values of wood based panels are 5-percentiles for strength values (f) and mean values for elastic properties (E, G). If necessary the 5-percentile values of the elastic properties can be calculated as 0.85 times the specified mean values.
  • Indices are given in the following way:
  • 1st index: indicates bending, tension, compression, shear or rolling shear as “m”, “t”, “c”, “v” or “r”
  • 2nd index: indicates orientation of stress to grain direction of outermost layers/veneers as “0” or”90”, if relevant
  • 3rd index: indicates, if in plane or out of plane; in plane is given as “edge”, out of plane is given as “flat” only in the case of stresses perpendicular to the grain and shear
  • 4th index: indicates characteristic “k” or mean value “mean”

Physikalische Eigenschaften

Name Wert Bemerkung Messverfahren und -bedingungen
Dichte > 650 kg/m³ nominal thickness: > 1.8mm – 12mm DIN EN 12369-1
> 600 kg/m³ nominal thickness: > 12mm – 19mm DIN EN 12369-1
> 550 kg/m³ nominal thickness: > 19mm – 30mm DIN EN 12369-1
> 500 kg/m³ nominal thickness: > 30mm DIN EN 12369-1
Differentielle Schwindung 0.71 – 0.93 %/% DIN EN 622-5, thickness
0.017 – 0.037 %/% DIN EN 622-5, length & width
Gleichgewichtsfeuchte 5.4 – 7.5 % DIN EN 622-5, relative humidity: 30 %
6.6 – 9.5 % DIN EN 622-5, relative humidity: 65 %
12.3 – 15.8 % DIN EN 622-5, relative humidity: 85 %
Modifikationsbeiwert 0.2 Service Class 1 DIN EN 622-5; DIN EN 1995-1-1, permanent
0.4 Service Class 1 DIN EN 622-5; DIN EN 1995-1-1, long term
0.6 Service Class 1 DIN EN 622-5; DIN EN 1995-1-1, medium term
0.8 Service Class 1 DIN EN 622-5; DIN EN 1995-1-1, short term
1.1 Service Class 1 DIN EN 622-5; DIN EN 1995-1-1, instantaneous
0.45 Service Class 2 DIN EN 622-5; DIN EN 1995-1-1, short term
0.8 Service Class 2 DIN EN 622-5; DIN EN 1995-1-1, instantaneous
Verformungsbeiwert 2.25 Service Class 1 DIN EN 622-5; DIN EN 1995-1-1
Wasserdampf-Diffusionswiderstandszahl 2 wet cup µ DIN EN 13986; DIN EN 622-5, density: 250 kg/m³
5 dry cup µ DIN EN 13986; DIN EN 622-5, density: 250 kg/m³
5 wet cup µ DIN EN 13986; DIN EN 622-5, density: 400 kg/m³
10 dry cup µ DIN EN 13986; DIN EN 622-5, density: 400 kg/m³
12 wet cup µ DIN EN 13986; DIN EN 622-5, density: 600 kg/m³
20 dry cup µ DIN EN 13986; DIN EN 622-5, density: 600 kg/m³
20 wet cup µ DIN EN 13986; DIN EN 622-5, density: 800 kg/m³
30 dry cup µ DIN EN 13986; DIN EN 622-5, density: 800 kg/m³
Mechanische Eigenschaften
 
Biege-Elastizitätsmodul 3700 MPa nominal thickness: > 1.8mm – 12mm DIN EN 12369-1, E[m,flat,mean] (perpendicular to plane)
3000 MPa nominal thickness: > 12mm – 19mm DIN EN 12369-1, E[m,flat,mean] (perpendicular to plane)
2900 MPa nominal thickness: > 19mm – 30mm DIN EN 12369-1, E[m,flat,mean] (perpendicular to plane)
2700 MPa nominal thickness: > 30mm DIN EN 12369-1, E[m,flat,mean] (perpendicular to plane)
Biegefestigkeit 21 MPa nominal thickness: > 1.8mm – 12mm DIN EN 12369-1, f[m,k] (perpendicular to plane)
21 MPa nominal thickness: > 12mm – 19mm DIN EN 12369-1, f[m,k] (perpendicular to plane)
21 MPa nominal thickness: > 19mm – 30mm DIN EN 12369-1, f[m,k] (perpendicular to plane)
19 MPa nominal thickness: > 30mm DIN EN 12369-1, f[m,k] (perpendicular to plane)
Druck-Elastizitätsmodul 2900 MPa nominal thickness: > 1.8mm – 12mm DIN EN 12369-1, E[c,edge,mean] (in plane)
2700 MPa nominal thickness: > 12mm – 19mm DIN EN 12369-1, E[c,edge,mean] (in plane)
2000 MPa nominal thickness: > 19mm – 30mm DIN EN 12369-1, E[c,edge,mean] (in plane)
1600 MPa nominal thickness: > 30mm DIN EN 12369-1, E[c,edge,mean] (in plane)
Druckfestigkeit 13 MPa nominal thickness: > 1.8mm – 12mm DIN EN 12369-1, f[c,edge,k] (in plane)
12.5 MPa nominal thickness: > 12mm – 19mm DIN EN 12369-1, f[c,edge,k] (in plane)
12 MPa nominal thickness: > 19mm – 30mm DIN EN 12369-1, f[c,edge,k] (in plane)
10 MPa nominal thickness: > 30mm DIN EN 12369-1, f[c,edge,k] (in plane)
Scherfestigkeit 6.5 MPa nominal thickness: > 1.8mm – 12mm DIN EN 12369-1, f[v,flat,k] (in plane)
6.5 MPa nominal thickness: > 12mm – 19mm DIN EN 12369-1, f[v,flat,k] (in plane)
6.5 MPa nominal thickness: > 19mm – 30mm DIN EN 12369-1, f[v,flat,k] (in plane)
5 MPa nominal thickness: > 30mm DIN EN 12369-1, f[v,flat,k] (in plane)
Schubmodul 800 MPa nominal thickness: > 1.8mm – 12mm DIN EN 12369-1, G[edge,mean] (perpendicular to plane)
800 MPa nominal thickness: > 12mm – 19mm DIN EN 12369-1, G[edge,mean] (perpendicular to plane)
800 MPa nominal thickness: > 19mm – 30mm DIN EN 12369-1, G[edge,mean] (perpendicular to plane)
600 MPa nominal thickness: > 30mm DIN EN 12369-1, G[edge,mean] (perpendicular to plane)
Zug-Elastizitätsmodul 2900 MPa nominal thickness: > 1.8mm – 12mm DIN EN 12369-1, E[t,mean]
2700 MPa nominal thickness: > 12mm – 19mm DIN EN 12369-1, E[t,mean]
2000 MPa nominal thickness: > 19mm – 30mm DIN EN 12369-1, E[t,mean]
1600 MPa nominal thickness: > 30mm DIN EN 12369-1, E[t,mean]
Zugfestigkeit 13 MPa nominal thickness: > 1.8mm – 12mm DIN EN 12369-1, f[t,k]
12.5 MPa nominal thickness: > 12mm – 19mm DIN EN 12369-1, f[t,k]
12 MPa nominal thickness: > 19mm – 30mm DIN EN 12369-1, f[t,k]
10 MPa nominal thickness: > 30mm DIN EN 12369-1, f[t,k]
Thermische Eigenschaften
 
Wärmeleitfähigkeit 0.05 W/(m*K) DIN EN 13986; DIN EN 622-5, density: 250 kg/m³
0.07 W/(m*K) DIN EN 13986; DIN EN 622-5, density: 400 kg/m³
0.1 W/(m*K) DIN EN 13986; DIN EN 622-5, density: 600 kg/m³
0.14 W/(m*K) DIN EN 13986; DIN EN 622-5, density: 800 kg/m³

Daten bereitgestellt von

Institut für Holztechnologie Dresden gemeinnützige GmbH

Institut für Holztechnologie Dresden gemeinnützige GmbH Steffen Tobisch
+493514662257
Anfrage per E-Mail

Haftungsausschluss

Die in diesem Dokument enthaltenen Informationen und Daten wurden entweder durch Prüfungen, Berechnungen oder Bewertungen vom Datenanbieter ermittelt und werden als korrekt erachtet. Die aufgeführten Werte sind jedoch beeinflussbar durch Verarbeitungsbedingungen, Modifikationen, Werkstoffzusätze und Umgebungseinflüsse und befreien den Anwender nicht von eigenen Prüfungen und Versuchen. Eine rechtlich verbindliche Zusicherung bestimmter Eigenschaften oder der Eignung für einen konkreten, insbesondere sicherheitsrelevanten Einsatzzweck durch den Datenanbieter kann aus den Angaben nicht abgeleitet werden.

Ähnliche Materialien

Wählen Sie die Materialeigenschaften aus, anhand derer ähnliche Materialien identifiziert werden sollen. Durch Hinzufügen weiterer Eigenschaften sowie Anpassen der jeweiligen Abweichung lässt sich die Ergebnisliste beeinflussen. Hier wird eine Auswahl der ähnlichsten Materialien angezeigt. Um die gesamte Liste zu erhalten, drücken Sie auf die Schaltfläche "Vollständige Ergebnisliste anzeigen".

5%

Letzte Aktualisierung: 31.08.2023