Cement Bonded Particleboard
Symbolbild
- Abkürzung: CBPB
- Deutsch: Spanplatte zementgebunden
- Characteristic Values of wood based panels are 5-percentiles for strength values (f) and mean values for elastic properties (E, G). If necessary the 5-percentile values of the elastic properties can be calculated as 0.85 times the specified mean values.
- Indices are given in the following way:
- 1st index: indicates bending, tension, compression, shear or rolling shear as “m”, “t”, “c”, “v” or “r”
- 2nd index: indicates orientation of stress to grain direction of outermost layers/veneers as “0” or”90”, if relevant
- 3rd index: indicates, if in plane or out of plane; in plane is given as “edge”, out of plane is given as “flat” only in the case of stresses perpendicular to the grain and shear
- 4th index: indicates characteristic “k” or mean value “mean”
Physikalische Eigenschaften
| Name | Wert | Bemerkung | Messverfahren und -bedingungen |
|---|---|---|---|
| Dichte | > 1160 kg/m³ | nominal thickness: 8mm – 40mm | |
| Differentielle Schwindung | 0.04 %/% | thickness | |
| 0.03 %/% | length | ||
| 0.03 %/% | width | ||
| Gleichgewichtsfeuchte | 5 % | relative humidity: 30 % | |
| 10 % | relative humidity: 65 % | ||
| 14 % | relative humidity: 85 % | ||
| Modifikationsbeiwert | 0.3 | Service Class 1 | DIN EN 1995-1-1/NA, permanent |
| 0.45 | Service Class 1 | DIN EN 1995-1-1/NA, long term | |
| 0.65 | Service Class 1 | DIN EN 1995-1-1/NA, medium term | |
| 0.85 | Service Class 1 | DIN EN 1995-1-1/NA, short term | |
| 1.1 | Service Class 1 | DIN EN 1995-1-1/NA, instantaneous | |
| 0.2 | Service Class 2 | DIN EN 1995-1-1/NA, permanent | |
| 0.3 | Service Class 2 | DIN EN 1995-1-1/NA, long term | |
| 0.45 | Service Class 2 | DIN EN 1995-1-1/NA, medium term | |
| 0.6 | Service Class 2 | DIN EN 1995-1-1/NA, short term | |
| 0.8 | Service Class 2 | DIN EN 1995-1-1/NA, instantaneous | |
| Verformungsbeiwert | 2.25 | Service Class 1 | DIN EN 1995-1-1/NA |
| 3 | Service Class 2 | DIN EN 1995-1-1/NA | |
| Wasserdampf-Diffusionswiderstandszahl | 30 | wet cup µ | DIN EN 13986; DIN EN 634-2, density: 1200 kg/m³ |
| 50 | dry cup µ | DIN EN 13986; DIN EN 634-2, density: 1200 kg/m³ | |
| Mechanische Eigenschaften | |||
| Biege-Elastizitätsmodul | 5200 MPa | nominal thickness: 8mm – 13mm | E[m,flat,mean] (perpendicular to plane) |
| 5100 MPa | nominal thickness: 8mm – 13mm | E[m,edge,mean] (in plane) | |
| 5400 MPa | nominal thickness: >13mm – 20mm | E[m,flat,mean] (perpendicular to plane) | |
| 4950 MPa | nominal thickness: >13mm – 20mm | E[m,edge,mean] (in plane) | |
| 5400 MPa | nominal thickness: > 20mm - 40mm | E[m,flat,mean] (perpendicular to plane) | |
| 4950 MPa | nominal thickness: > 20mm – 40mm | E[m,edge,mean] (in plane) | |
| Biegefestigkeit | 10.2 MPa | nominal thickness: 8mm – 13mm | f[m,k] (perpendicular to plane) |
| 10 MPa | nominal thickness: 8mm – 13mm | f[m,edge,k] (in plane) | |
| 9.2 MPa | nominal thickness: >13mm – 20mm | f[m,k] (perpendicular to plane) | |
| 8.7 MPa | nominal thickness: >13mm – 20mm | f[m,edge,k] (in plane) | |
| 8.3 MPa | nominal thickness: > 20mm - 40mm | f[m,k] (perpendicular to plane) | |
| 8.1 MPa | nominal thickness: > 20mm – 40mm | f[m,edge,k] (in plane) | |
| Druck-Elastizitätsmodul | 2250 MPa | nominal thickness: 8mm – 13mm | E[c,edge,mean] (in plane) |
| 3036 MPa | nominal thickness: >13mm – 20mm | E[c,edge,mean] (in plane) | |
| 3036 MPa | nominal thickness: > 20mm – 40mm | E[c,edge,mean] (in plane) | |
| Druckfestigkeit | 10 MPa | nominal thickness: 8mm – 13mm | f[c,flat,k] (perpendicular to plane) |
| 17 MPa | nominal thickness: 8mm – 13mm | f[c,edge,k] (in plane) | |
| 10 MPa | nominal thickness: >13mm – 20mm | f[c,flat,k] (perpendicular to plane) | |
| 14.6 MPa | nominal thickness: >13mm – 20mm | f[c,edge,k] (in plane) | |
| 10 MPa | nominal thickness: > 20mm - 40mm | f[c,flat,k] (perpendicular to plane) | |
| 14.2 MPa | nominal thickness: > 20mm – 40mm | f[c,edge,k] (in plane) | |
| Scherfestigkeit | 9.3 MPa | nominal thickness: 8mm – 13mm | f[v,edge,k] (perpendicular to plane) |
| 3 MPa | nominal thickness: 8mm – 13mm | f[v,flat,k] (in plane) | |
| 7.5 MPa | nominal thickness: >13mm – 20mm | f[v,edge,k] (perpendicular to plane) | |
| 2.5 MPa | nominal thickness: >13mm – 20mm | f[v,flat,k] (in plane) | |
| 7.2 MPa | nominal thickness: > 20mm - 40mm | f[v,edge,k] (perpendicular to plane) | |
| 2.5 MPa | nominal thickness: > 20mm – 40mm | f[v,flat,k] (in plane) | |
| Schubmodul | 2200 MPa | nominal thickness: 8mm – 13mm | G[flat,mean] (in plane) |
| 2040 MPa | nominal thickness: >13mm – 20mm | G[flat,mean] (in plane) | |
| 2040 MPa | nominal thickness: > 20mm – 40mm | G[flat,mean] (in plane) | |
| Zug-Elastizitätsmodul | 4900 MPa | nominal thickness: 8mm – 13mm | E[t,mean] |
| 4800 MPa | nominal thickness: >13mm – 20mm | E[t,mean] | |
| 4800 MPa | nominal thickness: > 20mm – 40mm | E[t,mean] | |
| Zugfestigkeit | 4.3 MPa | nominal thickness: 8mm – 13mm | f[t,k] |
| 3.9 MPa | nominal thickness: >13mm – 20mm | f[t,k] | |
| 3.6 MPa | nominal thickness: > 20mm – 40mm | f[t,k] | |
| Thermische Eigenschaften | |||
| Wärmeleitfähigkeit | 0.23 – 0.35 W/(m*K) | DIN EN 13986; DIN EN 634-2, density: 1200 kg/m³ | |
Daten bereitgestellt von
Institut für Holztechnologie Dresden gemeinnützige GmbH
Institut für Holztechnologie Dresden gemeinnützige GmbH Steffen Tobisch
+493514662257
Anfrage per E-Mail
Webseite | Mehr Details | Zu den Materialien von Institut für Holztechnologie Dresden gGmbH
Die in diesem Dokument enthaltenen Informationen und Daten wurden entweder durch Prüfungen, Berechnungen oder Bewertungen vom Datenanbieter ermittelt und werden als korrekt erachtet. Die aufgeführten Werte sind jedoch beeinflussbar durch Verarbeitungsbedingungen, Modifikationen, Werkstoffzusätze und Umgebungseinflüsse und befreien den Anwender nicht von eigenen Prüfungen und Versuchen. Eine rechtlich verbindliche Zusicherung bestimmter Eigenschaften oder der Eignung für einen konkreten, insbesondere sicherheitsrelevanten Einsatzzweck durch den Datenanbieter kann aus den Angaben nicht abgeleitet werden.
Ähnliche Materialien
Wählen Sie die Materialeigenschaften aus, anhand derer ähnliche Materialien identifiziert werden sollen. Durch Hinzufügen weiterer Eigenschaften sowie Anpassen der jeweiligen Abweichung lässt sich die Ergebnisliste beeinflussen. Hier wird eine Auswahl der ähnlichsten Materialien angezeigt. Um die gesamte Liste zu erhalten, drücken Sie auf die Schaltfläche "Vollständige Ergebnisliste anzeigen".