Alloy M25 (17300) (Kupfer-Beryllium-Legierung)

Alloy M25 from Materion is a free machining, high performance copper alloy. M25’s properties minimize signal distortion in coaxial RF connectors and reduce power loss in circular connectors and contact probes. M25 is available in straight rod or coiled wire product forms, and in different tempers to accommodate diverse design requirements. After machining and forming operations, M25 parts can be easily heat treated and plated to obtain maximum mechanical and electrical performance. Applications requiring stability to 175° C or reliable contact force in miniaturized designs specify Alloy M25. In demanding electronic applications, M25 provides performance and reliability superior to any free machining copper alloy.

Weitere Informationen finden Sie hier.

Abbildung des Materials
Bauform Stangen; gewickelter Draht
alternative Namen
  • Abkürzung: C17300, ASTM B-196, ASTM B-197, EN 12164, EN 12165, EN 12166, MIL-C-21657
  • Englisch: Copper Beryllium Alloy

Physikalische Eigenschaften

Name Wert Messverfahren und -bedingungen
Dichte 8.36 g/cm³ nach Wärmebehandlung
8.3 g/cm³ vor Wärmebehandlung
Mechanische Eigenschaften
 
0,2-%-Streckgrenze bei Zugbeanspruchung 130 – 250 MPa Stange / vor Wärmebehandlung (A (TB00)) / D = 0.76 mm bis 63.5 mm
520 – 720 MPa Stange / vor Wärmebehandlung (H (TD04)) / D = 0.76 mm bis 9.5 mm
520 – 720 MPa Stange / vor Wärmebehandlung (H (TD04)) / D = 9.5 mm bis 25.4 mm
520 – 720 MPa Stange / vor Wärmebehandlung (H (TD04)) / D = 25.4 mm bis 63.5 mm
1000 – 1210 MPa Stange / Wärmebehandlung (AT (TF00)): 315 °C - 357 °C, 3 h / D = 0.76 mm bis 63.5 mm
1100 – 1380 MPa Stange / Wärmebehandlung (HT (TH04)): 315 °C - 357 °C, 2 h - 3 h / D = 0.76 mm bis 9.5 mm
1070 – 1340 MPa Stange / Wärmebehandlung (HT (TH04)): 315 °C - 357 °C, 2 h - 3 h / D = 9.5 mm bis 25.4 mm
1000 – 1310 MPa Stange / Wärmebehandlung (HT (TH04)): 315 °C - 357 °C, 2 h - 3 h / D = 25.4 mm bis 36.5 mm
130 – 210 MPa Draht / vor Wärmebehandlung (A (TB00))
510 – 730 MPa Draht / vor Wärmebehandlung (1/4 H (TD01))
620 – 870 MPa Draht / vor Wärmebehandlung (1/2 H (TD02))
790 – 1040 MPa Draht / vor Wärmebehandlung (3/4 H (TD03))
890 – 1110 MPa Draht / vor Wärmebehandlung (H (TD04))
990 – 1250 MPa Draht / Wärmebehandlung (AT (TF00)): 315 °C - 330 °C, 3 h
1130 – 1380 MPa Draht / Wärmebehandlung (1/4 HT (TH01)): 315 °C - 330 °C, 2 h
1170 – 1450 MPa Draht / Wärmebehandlung (1/2 HT (TH02)): 315 °C - 330 °C, 1.5 h
1200 – 1520 MPa Draht / Wärmebehandlung (3/4 HT (TH03)): 315 °C - 330 °C, 1 h
1240 – 1520 MPa Draht / Wärmebehandlung (HT (TH04)): 315 °C - 330 °C, 1 h
Zug-Elastizitätsmodul 131 GPa
Zugdehnung beim Bruch 20 – 75 % Stange / vor Wärmebehandlung (A (TB00)) / D = 0.76 mm bis 63.5 mm
8 – 30 % Stange / vor Wärmebehandlung (H (TD04)) / D = 0.76 mm bis 9.5 mm
8 – 30 % Stange / vor Wärmebehandlung (H (TD04)) / D = 9.5 mm bis 25.4 mm
8 – 20 % Stange / vor Wärmebehandlung (H (TD04)) / D = 25.4 mm bis 63.5 mm
4 – 10 % Stange / Wärmebehandlung (AT (TF00)): 315 °C - 357 °C, 3 h / D = 0.76 mm bis 63.5 mm
2 – 9 % Stange / Wärmebehandlung (HT (TH04)): 315 °C - 357 °C, 2 h - 3 h / D = 0.76 mm bis 9.5 mm
2 – 9 % Stange / Wärmebehandlung (HT (TH04)): 315 °C - 357 °C, 2 h - 3 h / D = 9.5 mm bis 25.4 mm
4 – 9 % Stange / Wärmebehandlung (HT (TH04)): 315 °C - 357 °C, 2 h - 3 h / D = 25.4 mm bis 63.5 mm
30 – 75 % Draht / vor Wärmebehandlung (A (TB00))
2 – 25 % Draht / vor Wärmebehandlung (1/4 H (TD01))
2 – 15 % Draht / vor Wärmebehandlung (1/2 H (TD02))
2 – 8 % Draht / vor Wärmebehandlung (3/4 H (TD03))
1 – 8 % Draht / vor Wärmebehandlung (H (TD04))
> 3 % Draht / Wärmebehandlung (AT (TF00)): 315 °C - 330 °C, 3 h
> 2 % Draht / Wärmebehandlung (1/4 HT (TH01)): 315 °C - 330 °C, 2 h
> 2 % Draht / Wärmebehandlung (1/2 HT (TH02)): 315 °C - 330 °C, 1.5 h
> 2 % Draht / Wärmebehandlung (3/4 HT (TH03)): 315 °C - 330 °C, 1 h
> 1 % Draht / Wärmebehandlung (HT (TH04)): 315 °C - 330 °C, 1 h
Zugfestigkeit 410 – 590 MPa Stange / vor Wärmebehandlung (A (TB00)) / D = 0.76 mm bis 63.5 mm
620 – 900 MPa Stange / vor Wärmebehandlung (H (TD04)) / D = 0.76 mm bis 9.5 mm
620 – 860 MPa Stange / vor Wärmebehandlung (H (TD04)) / D = 9.5 mm bis 25.4 mm
590 – 830 MPa Stange / vor Wärmebehandlung (H (TD04)) / D = 25.4 mm bis 63.5 mm
1140 – 1380 MPa Stange / Wärmebehandlung (AT (TF00)): 315 °C - 357 °C, 3 h / D = 0.76 mm bis 63.5 mm
1280 – 1550 MPa Stange / Wärmebehandlung (HT (TH04)): 315 °C - 357 °C, 2 h - 3 h / D = 0.76 mm bis 9.5 mm
1240 – 1520 MPa Stange / Wärmebehandlung (HT (TH04)): 315 °C - 357 °C, 2 h - 3 h / D = 9.5 mm bis 25.4 mm
1210 – 1480 MPa Stange / Wärmebehandlung (HT (TH04)): 315 °C - 357 °C, 2 h - 3 h / D = 25.4 mm bis 63.5 mm
410 – 565 MPa Draht / vor Wärmebehandlung (A (TB00))
620 – 800 MPa Draht / vor Wärmebehandlung (1/4 H (TD01))
750 – 940 MPa Draht / vor Wärmebehandlung (1/2 H (TD02))
890 – 1070 MPa Draht / vor Wärmebehandlung (3/4 H (TD03))
960 – 1140 MPa Draht / vor Wärmebehandlung (H (TD04))
1100 – 1380 MPa Draht / Wärmebehandlung (AT (TF00)): 315 °C - 330 °C, 3 h
1200 – 1450 MPa Draht / Wärmebehandlung (1/4 HT (TH01)): 315 °C - 330 °C, 2 h
1270 – 1490 MPa Draht / Wärmebehandlung (1/2 HT (TH02)): 315 °C - 330 °C, 1.5 h
1310 – 1590 MPa Draht / Wärmebehandlung (3/4 HT (TH03)): 315 °C - 330 °C, 1 h
1340 – 1590 MPa Draht / Wärmebehandlung (HT (TH04)): 315 °C - 330 °C, 1 h
Elektrische und magnetische Eigenschaften
 
elektrische Leitfähigkeit 5.9 – 6.9 1/(µΩ*cm) Stange
6.2 – 7.8 1/(µΩ*cm) Draht
spezifischer elektrischer Widerstand 5.9 – 6.9 µΩ*cm Stange
6.2 – 7.8 µΩ*cm Draht
Thermische Eigenschaften
 
linearer Längenausdehnungskoeffizient 1.75E-5 m/(m*°C)
Schmelztemperatur 870 °C Solidustemperatur
Wärmeleitfähigkeit 105 W / (m K) 25 °C

Chemische Eigenschaften

chemische Zusammensetzung (Gewichtsprozent)
Be

1.80 - 2.00 %

Ni + Co

> 0.20 %

Ni + Co + Fe

< 0.6 %

Pb

0.20 - 0.60 %

Cu

Rest %

Freigaben

Regularium Land Bauteil Bemerkungen Gültig bis Prüfzeugnis
Verordnung (EG) 1935/2004 EU konform 09/2021 Dokument
§§30 und §§31 Lebensmittel-, Bedarfsgegenstände- und Futtermittelgesetzbuch (LFGB) D konform 09/2021 Dokument
Verordnung (EU) 10/2011 EU konform 09/2021 Dokument

Hersteller

Materion Brush GmbH

Daten bereitgestellt von

Materion Brush GmbH

Allgemeine Kontaktdaten Materion Brush GmbH
0711830930
Anfrage per E-Mail

Haftungsausschluss

Only the buyer can determine the appropriateness of any processing practice, end-product or application. Materion does not make any warranty regarding its recommendations, the suitability of Materion's product, or its processing suggestions for buyer's end product, application or equipment. The properties presented on this data sheet are for reference purposes only, intended only to initiate the material selection process. They do not constitute, nor are they intended to constitute, a material specification. Material will be produced to one of the applicable industry standards, if any, listed in the Industry Standards and Specification section. Actual properties may vary by thickness and/or part number. Please contact your local sales engineer for detailed properties to be used in simulation. Any properties marked as preliminary are subject to change at any time as the manufacturing process is further refined.

Ähnliche Materialien

Wählen Sie die Materialeigenschaften aus, anhand derer ähnliche Materialien identifiziert werden sollen. Durch Hinzufügen weiterer Eigenschaften sowie Anpassen der jeweiligen Abweichung lässt sich die Ergebnisliste beeinflussen. Hier wird eine Auswahl der ähnlichsten Materialien angezeigt. Um die gesamte Liste zu erhalten, drücken Sie auf die Schaltfläche "Vollständige Ergebnisliste anzeigen".

5%

Letzte Aktualisierung: 05.11.2021
Feedback

Geben Sie uns gern Feedback zum Material Hub.

Kontaktformular

Fragebogen zur Gebrauchstauglichkeit

QR Code